ПредпросмотрThis document specifies requirements for non-electrolytically applied zinc flake coating systems for steel fasteners. It is applicable to coatings:
— with or without hexavalent chromium;
— with or without top coat;
— with or without lubricant (integral lubricant and/or subsequently added lubricant).
It is applicable to bolts, screws, studs and nuts with ISO metric thread, to fasteners with non-ISO metric thread, and to non-threaded fasteners such as washers, pins, clips, etc.
This document does not specify requirements for such fastener properties as weldability or paintability. It is not applicable to mechanically applied zinc coatings.
NOTE Coatings in accordance with this document are especially used for high strength fasteners (≥ 1 000 MPa) to avoid risk of internal hydrogen embrittlement (IHE — see 4.4).
Information for design and assembly of coated fasteners is given in Annex A.
-
Текущий статус: PublishedДата публикации: 2018-08
-
Версия: 3
Приобрести данный стандарт
| Формат | Язык | |
|---|---|---|
| std 1 145 | PDF + ePub | |
| std 2 145 | Бумажный |
- CHF145
Жизненный цикл
-
Ранее
WithdrawnISO 10683:2014
-
Сейчас
PublishedISO 10683:2018
Стандарт, который пересматривается каждые 5 лет
Этап: 90.20 (Hа стадии пересмотра)-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00
Появились вопросы?
Ознакомьтесь с FAQ
Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)
Будьте в курсе актуальных новостей ИСО
Подписывайтесь на наши новости, обзоры, а также на информацию о продуктах.